5454 aluminium–magnesium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). It is closely related to 5154 aluminium alloy. As an aluminium-magnesium alloy, it combines moderate-to-high strength with excellent weldability. Like 5154, 5454 aluminium is commonly used in welded structures such as pressure vessels and ships. As a wrought alloy, it can be formed by rolling, extrusion, and forging (although forging is not common), but not casting. It can be cold worked to produce tempers with a higher strength but a lower ductility. It is generally not clad.Marks' Standard Handbook for Mechanical Engineers, 8th Ed., McGraw-Hill, pp. 6-50 to 6-57
Alternate names and designations include 3.3537, N51, and A95454. The alloy and its various tempers are covered by the following standards:5454 (3.3537, N51, A95454) Aluminum. Retrieved on 2014-12-04.
ASTM B 209: Standard Specification for Aluminium and Aluminium-Alloy Sheet and Plate ASTM B 221: Standard Specification for Aluminium and Aluminium-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes ASTM B 547: Standard Specification for Aluminium and Aluminium-Alloy Formed and Arc-Welded Round Tube ISO 6361: Wrought Aluminium and Aluminium Alloy Sheets, Strips and Plates
Chemical composition
The alloy composition of 5454 aluminium is:
Aluminium: 94.5 to 97.1% Chromium: 0.05 to 0.20% Copper: 0.1% max Iron: 0.4% max Magnesium: 2.4 to 3.0% Manganese: 0.5 to 1.0% Silicon: 0.25% max Titanium: 0.2% max Zinc: 0.25% max Residuals: 0.15% max
Properties
Typical material properties for 5454 aluminium alloy include:
Density: 2.69 g/cm3, or 168 lb/ft3. Young's modulus: 70 GPa, or 10 Msi. Electrical conductivity: 34% IACS. Ultimate tensile strength: 240 to 300 MPa, or 35 to 44 ksi. Thermal Conductivity: 130 W/m-K. Thermal Expansion: 22.3 μm/m-K.